Just curious why the hot allowable (Sh) for 1.4903 material at 550 deg. C at 100,000 hrs = 109282.070 KPa (1.4903S-16-100) while at 200,000 hrs = 122335.234 KPa (1.4903S-16-200).

My thought is that for longer service life the level of stress must be lower.

Please correct my interpretation.