Hello dear engineer. Hope to be OK. These days I need to work on borosilicate glass piping. So i need to model a glass tower and its piping. is it acceptable to model in Caesar ii? which code do you suggest ?ASME B31.3?OR DIN?
PLEASE GIVE ME SOME ADVICE.
BEST REGARD

Glass, like any other amorphous elastic material should be ok to model in Caesar. Just get the correct properties.

Glass pipework obviously has special needs regarding support, attachements, joints etc.

As regards the Code to apply, it's probably not your choice. See project documents or talk to the operator.

Crystal clear I hope.

thanks for advice